LNP VERTON RV007ESS is a compound based on Polyamide 66 (Nylon 66) resin containing 35% long glass fiber. Added features include Easy Molding, Structural and Heat Stabilized.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 277 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 25 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 290 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 280 - 295 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 204 | MPa | ASTM D638 |
| Flexural Modulus | 9880 | MPa | ASTM D790 |
| Tensile Stress, break | 214 | MPa | ISO 527 |
| Tensile Strain, break | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11970 | MPa | ISO 527 |
| Flexural Stress | 309 | MPa | ISO 178 |
| Flexural Modulus | 10240 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.97 | % | ASTM D570 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 245 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 252 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 95 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |