LNP VERTON RV008ES is a compound based on Polyamide 66 (Nylon 66) resin containing 40% long glass fiber. Added features include Easy Molding, Heat Stabilized and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1072 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 273 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 72 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 26 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 26 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 93 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 290 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 280 - 295 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 86.5 | MPa | ASTM D638 |
| Tensile Stress, break | 130 | MPa | ASTM D638 |
| Tensile Strain, yield | 0.7 | % | ASTM D638 |
| Tensile Strain, break | 1.2 | % | ASTM D638 |
| Flexural Stress | 310 | MPa | ASTM D790 |
| Flexural Modulus | 10500 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 223 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14100 | MPa | ISO 527 |
| Flexural Stress | 322 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage, xflow | 0.4 - 0.6 | % | SABIC method |
| Water Absorption, (23°C/24hrs) | 1.2 | % | ISO 62-1 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Density | 1.46 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 80°C, flow | 2.00E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.30E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, flow | 2.10E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.10E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 257 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/120 | 250 | °C | ISO 306 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 252 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 251 | °C | ISO 75/Af |