LNP VERTON RV00AES is a compound based on Polyamide 66 (Nylon 66)resin containing 50% long glass fiber. Added features include Easy Molding, Heat Stabilized and Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 5 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥0.75 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.75 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 0 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 0 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.75 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 384 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 |
| Multiaxial Impact | 15 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 90 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 38 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 290 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 280 - 295 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 254 | MPa | ASTM D638 |
| Tensile Strain, break | 1.9 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 17510 | MPa | ASTM D638 |
| Flexural Stress | 374 | MPa | ASTM D790 |
| Flexural modulus | 14160 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 276 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 276 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 18100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 366 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 15000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.22 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ISO 294 |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.9 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 241 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.85E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.86E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 259 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 255 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 110 | °C | UL 746B |