LNP VERTON RV00AEU is a compound based on Polyamide 66 (Nylon 66) resin containing 50% long glass fiber. Added features include Easy Molding, UV Stabilized and Structural.
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 90 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 290 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 300 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 280 - 295 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 276 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 276 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 17800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 366 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 15000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow, 24 hrs | 0.15 - 0.35 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ISO 294 |
| Density | 1.6 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.9 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 259 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 256 | °C | ISO 75/Af |