LNP™ VERTON™ Compound RVL28

LNP VERTON RVL28 is a compound based on Polyamide 66 (Nylon 66) resin containing 40% long glass fiber, 10% PTFE. Added features include Easy Molding, Heat Stabilized, Wear Resistant and Structural.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
Heat Stabilized
High stiffness/Strength
Wear resistant

Industry

Material previously used in

Automotive Exteriors
Building Component
Electrical
Home Appliances
Industrial General
Sport/Leisure

Applications

Possible usage of material

Lab Ware and Clinical Diagnostics
Monitoring and Imaging
Power Boat

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	23	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	93	kJ/m²	ISO 180/1U
Multiaxial Impact	7	J	ISO 6603
Izod Impact, notched, 23°C	265	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1409	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	14	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	290 - 305	°C
Front - Zone 3 Temperature	290 - 300	°C
Middle - Zone 2 Temperature	290 - 300	°C
Rear - Zone 1 Temperature	280 - 295	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	228	MPa	ISO 527
Tensile Stress, break	228	MPa	ISO 527
Tensile Strain, yield	2.4	%	ISO 527
Tensile Strain, break	2.4	%	ISO 527
Tensile Modulus, 1 mm/min	13230	MPa	ISO 527
Flexural Stress	351	MPa	ISO 178
Flexural Modulus	13000	MPa	ISO 178
Tensile Stress, yield	220	MPa	ASTM D638
Tensile Stress, break	220	MPa	ASTM D638
Tensile Strain, yield	2.3	%	ASTM D638
Tensile Strain, break	2.3	%	ASTM D638
Tensile Modulus, 50 mm/min	14470	MPa	ASTM D638
Flexural Stress	337	MPa	ASTM D790
Flexural modulus	12200	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.57	g/cm³	ISO 1183
Mold Shrinkage, flow, 24 hrs	0.33	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.77	%	ISO 294
Density	1.57	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.5	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	259	°C	ISO 75/Bf
CTE, -40°C to 40°C, flow	2.10E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.90E-05	1/°C	ISO 11359-2
HDT, 0.45 MPa, 3.2 mm, unannealed	256	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	252	°C	ASTM D648
CTE, -40°C to 40°C, flow	2.16E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	4.86E-05	1/°C	ASTM E831

Register for High value Multi-Point Data