LNP™ VERTON™ Compound RVL29U

LNP VERTON RVL29U is a compound based on Polyamide 66 (Nylon 66) resin containing 45% long glass fiber, 10% PTFE. Added features include UV stabilized, Wear Resistant and Structural.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Wear resistant
Weatherable/UV stable

Industry

Material previously used in

Automotive Exteriors
Building Component
Commercial Appliance
Electrical
Home Appliances
Industrial General
Sport/Leisure

Applications

Possible usage of material

Lawn/Garden

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	27	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	27	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	81	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	76	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	31	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	80	kJ/m²	ISO 179/1eU
Multi-Axial Instrumented Impact Total Energy, 23°C	12	J	ISO 6603-2
Izod Impact, notched, 23°C	170	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1090	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	10	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Hopper Temperature	40	°C
Melt Temperature	290 - 305	°C
Rear - Zone 1 Temperature	280 - 295	°C
Middle - Zone 2 Temperature	290 - 300	°C
Front - Zone 3 Temperature	290 - 300	°C
Nozzle Temperature	290 - 305	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	16000	MPa	ISO 527
Tensile Stress, break, 5 mm/min	230	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Flexural Modulus, 2 mm/min	13000	MPa	ISO 178
Flexural Strength, 2 mm/min	330	MPa	ISO 178
Hardness, Rockwell R	115	-	ISO 2039-2
Hardness, Rockwell M	112	-	ISO 2039-2
Hardness, Rockwell L	96	-	ISO 2039-2
Tensile Modulus, 5 mm/min	16000	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	220	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.8	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	12800	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	320	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.64	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.4 - 0.6	%	ISO 62-4
Water Absorption, (23°C/saturated)	3.2 - 3.8	%	ISO 62-1
Specific Gravity	1.66	-	ASTM D792
Wear Factor Washer	25	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Instr.
Dynamic COF	0.42	-	ASTM D3702 Modified: Instr.
Static COF	0.48	-	ASTM D3702 Modified: Instr.
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.7 - 0.9	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	255	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	260	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	247	°C	ISO 306
Vicat Softening Temp, Rate B/120	253	°C	ISO 306
CTE, -40°C to 40°C, flow	1.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.0E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES