LNP™ VERTON™ Compound RVN1AESP

LNP VERTON RVN1AESP is a compound based on Polyamide 66 (Nylon 66) resin containing 50% long glass fiber and proprietary lubricant. Added features include Easy Molding, Wear Resistant and Structural.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Automotive Exteriors
Building Component
Commercial Appliance
Electrical
Home Appliances
Industrial General
Sport/Leisure

Applications

Possible usage of material

Oil/Gas

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1160	J/m	ASTM D4812
Izod Impact, notched, 23°C	270	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	12	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	35	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	40	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	90	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	35	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	95	kJ/m²	ISO 179/1eU
Multiaxial Impact	13	J	ISO 6603

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Drying Time (Cumulative)	48	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	290 - 305	°C
Nozzle Temperature	290 - 305	°C
Front - Zone 3 Temperature	290 - 300	°C
Middle - Zone 2 Temperature	290 - 300	°C
Rear - Zone 1 Temperature	280 - 295	°C
Hopper Temperature	40	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	250	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.1	%	ASTM D638
Tensile Modulus, 5 mm/min	16700	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	320	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	11800	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	235	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.4	%	ISO 527
Tensile Modulus, 1 mm/min	17000	MPa	ISO 527
Flexural Strength, 2 mm/min	330	MPa	ISO 178
Flexural Modulus, 2 mm/min	11300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption, (23°C/50% RH/24 hrs)	0.1	%	ASTM D570
Water Absorption, (23°C/24hrs)	0.8 - 0.9	%	ASTM D570
Specific Gravity	1.6	-	ASTM D792
Density	1.6	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.3	%	ISO 62
Water Absorption, (23°C/saturated)	4.4	%	ISO 62-1
Mold Shrinkage, flow, 24 hrs	0.2 - 0.3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.8	%	ISO 294
Wear Factor Washer	33	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Instr.
Dynamic COF	0.58	-	ASTM D3702 Modified: Instr.
Static COF	0.71	-	ASTM D3702 Modified: Instr.

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	240	°C	ISO 306
Vicat Softening Temp, Rate B/120	235	°C	ISO 306
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	250	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	245	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	1.4E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.7E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES