LNP VERTON UX03320 is a compound based on Polyphthalamide (PPA) resin containing 50% long glass fiber and proprietary fillers. Added feature of this grade is Structural.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.8 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 800 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 300 | J/m | ASTM D256 |
| Multiaxial Impact | 19 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 38 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 | % | |
| Melt Temperature | 315 - 330 | °C | |
| Front - Zone 3 Temperature | 330 - 345 | °C | |
| Middle - Zone 2 Temperature | 320 - 330 | °C | |
| Rear - Zone 1 Temperature | 315 - 325 | °C | |
| Mold Temperature | 140 - 165 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 220 | MPa | ASTM D638 |
| Tensile Strain, break | 1.9 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 18200 | MPa | ASTM D638 |
| Flexural Stress | 300 | MPa | ASTM D790 |
| Flexural Modulus | 18000 | MPa | ASTM D790 |
| Tensile Stress, break | 200 | MPa | ISO 527 |
| Tensile Strain, break | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 20300 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 360 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 17700 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.05 - 0.1 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.08 - 0.2 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.06 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.15 | % | ISO 294 |
| Spiral flow (1mm) | 30 | cm | SABIC method |
| Spiral flow (3mm) | 70 | cm | SABIC method |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 260 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 2.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 2.2E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 275 | °C | ISO 75/Af |