IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -40°C | 36 | kJ/m² | ISO 180/1A |
LNP VERTON WV006 is a compound based on Polybutylene Terephthalate (PBT) resin containing 30% long glass fiber. Added feature of this grade is Structural.
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -40°C | 36 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 250 - 260 | °C | |
Front - Zone 3 Temperature | 250 - 260 | °C | |
Middle - Zone 2 Temperature | 240 - 250 | °C | |
Rear - Zone 1 Temperature | 230 - 245 | °C | |
Mold Temperature | 65 - 120 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 70 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 187 | MPa | ISO 527 |
Tensile Strain, break | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 11570 | MPa | ISO 527 |
Flexural Stress | 247 | MPa | ISO 178 |
Flexural Modulus | 9780 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.54 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Af |