NORYL GTX™ Resin 9F0051XT

NORYL GTX 9F0051XT resin is a 25% glass fiber reinforced polyamide-based compound, with high modulus, high strength, high heat resistance and good dimensional stability with low CTE. This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at ≥ 1.5mm and 5VB at ≥ 2.0mm. The target application is various industrial and automotive electric components, including connector, sensor, EV battery module and busbar insulator.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
High stiffness/Strength
High temperature resistance
Low Warpage
No PFAS intentionally added
Non halogenated flame retardant

Industry

Material previously used in

Electrical
Energy Storage

Applications

Possible usage of material

Auto Electrical
Energy Management
EV/HEV Battery

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.4E+15	Ω.cm	ASTM D257
Surface Resistivity	4.3E+15	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥1.5	mm	UL 94
UL Recognized, 94-5VB Flame Class Rating	≥2.0	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	74	J/m	ASTM D256
Izod Impact, unnotched, 23°C	605	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	7.7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	38	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 5	Hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	260 - 320	°C
Nozzle Temperature	250 - 320	°C
Front - Zone 3 Temperature	260 - 320	°C
Middle - Zone 2 Temperature	260 - 320	°C
Rear - Zone 1 Temperature	260 - 320	°C
Mold Temperature	75 - 150	°C
Back Pressure	0.2 - 1.6	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	20 - 60	%
Vent Depth	0.013 - 0.045	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	132	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.7	%	ASTM D638
Tensile Modulus, 5 mm/min	9400	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	196	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	8240	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	131	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.9	%	ISO 527
Tensile Modulus, 1 mm/min	9412	MPa	ISO 527
Flexural Strength, 2 mm/min	186	MPa	ISO 178
Flexural Modulus, 2 mm/min	7727	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.35	g/cm³	ISO 1183
Melt Flow Rate, 280°C/5.0 kgf	20	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/5.0 kgf	33	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/5.0 kg	17.6	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/5.0 kg	33	cm³/10 min	ISO 1133
Water Absorption, 23°C/24hrs	0.59	%	SABIC method
Moisture Absorption, (23°C/50% RH/24 hrs)	0.16	%	ASTM D570
Moisture Absorption, (23°C/50% RH/24hrs)	0.15	%	ISO 62-4
Mold Shrinkage, flow	0.5	%	SABIC method
Mold Shrinkage, xflow	0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	254	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	238	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	253	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	239	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	2.7E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.6E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.4E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	65	°C	UL 746B
Relative Temp Index, Mech w/impact	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	65	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES