NORYL GTX™ Resin GTX1089

Sustainable Grade

NORYL GTX1089 resin is a sustainable low CO2 footprint, conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized for primer-less electrostatic painting. NORYL GTX1089 resin exhibits low water uptake, high heat resistance and high impact resistance. This material is intended for automotive applications such as body panels, tank flaps, fenders, trunk lid, and exterior trim.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Chemical Resistance
Dimensional stability
Electrically Conductive
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Sustainable (bio-based offerings)

Industry

Material previously used in

Automotive Exteriors

Applications

Possible usage of material

Exterior

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

Electrical properties

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume resistivity	5.E+03	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	21	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	137	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	23	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	262	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	46	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.07	%
Melt Temperature	290 - 320	°C
Rear - Zone 1 Temperature	260 - 280	°C
Middle - Zone 2 Temperature	280 - 300	°C
Front - Zone 3 Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Mold Temperature	100 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2250	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	56	MPa	ISO 527
Tensile Stress, break, 50 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Nominal Strain, break, 50 mm/min	65	%	ISO 527
Flexural Modulus, 2 mm/min	1950	MPa	ISO 178
Flexural Strength, 2 mm/min	78	MPa	ISO 178
Tensile Modulus, 50 mm/min	2220	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	59	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.5	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	55	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2070	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	87	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.07	g/cm³	ISO 1183
Melt Volume Rate, MVR at 280°C/5.0 kg	12	cm³/10 min	ISO 1133
Moisture Absorption, (23°C/50% RH/24hrs)	0.1	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.8	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.3	%	ISO 62-1
Water Absorption, (23°C/saturated)	2.4	%	ISO 62-1
Melt Flow Rate, 280°C/5.0 kgf	13	g/10 min	ASTM D1238
Specific Gravity	1.07	-	ASTM D792
Mold Shrinkage, flow	1.5	%	SABIC method
Mold Shrinkage, xflow	1.3	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	176	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	182	°C	ISO 306
Vicat Softening Temp, Rate B/120	183	°C	ISO 306
CTE
– CTE, -40°C to 100°C, flow	1.1E-04	1/°C	ISO 11359-2
– CTE, -40°C to 100°C, xflow	1.1E-04	1/°C	ISO 11359-2
– CTE, -40°C to 100°C, flow	1.1E-04	1/°C	ASTM E831
– CTE, -40°C to 100°C, xflow	1.1E-04	1/°C	ASTM E831
HDT, 0.45 MPa, 3.2 mm, unannealed	178	°C	ASTM D648
Vicat Softening Temp, Rate B/50	182	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	186	°C	ASTM D1525

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES