IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 88 | J/m | ASTM D256 |
NORYL GTX6801 resin is a 30% glass fiber reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 8430MPa), excellent chemical resistance, and high heat resistance. NORYL GTX6801 resin is an excellent candidate for industrial applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 88 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 140 | °C | |
Drying Time | 2 - 4 | Hrs | |
Melt Temperature | 275 - 290 | °C | |
Nozzle Temperature | 275 - 290 | °C | |
Front - Zone 3 Temperature | 275 - 290 | °C | |
Middle - Zone 2 Temperature | 265 - 280 | °C | |
Rear - Zone 1 Temperature | 260 - 270 | °C | |
Mold Temperature | 80 - 120 | °C | |
Screw Speed | 30 - 80 | rpm | |
Back Pressure | 0.5 - 1.5 | MPa |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 157 | MPa | SABIC - Japan Method |
Tensile Strain, break | 10 | % | SABIC - Japan Method |
Flexural Stress | 216 | MPa | ASTM D790 |
Flexural Modulus | 8430 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.33 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.5 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.7 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 24.2 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 6.4 mm, unannealed | 230 | °C | ASTM D648 |
CTE, -30°C to 30°C | 0.00003 - 0.00005 | 1/°C | TMA |