NORYL GTX830N resin is a 30% glass fiber reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 8200 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX830 resin is an excellent candidate for a wide variety of applications including automotive under the bonnet applications and water meter housings.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Arc Resistance, Tungsten {PLC} | 4 | PLC Code | ASTM D495 |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| Volume Resistivity | 1.0E+13 | Ω.cm | IEC 60093 |
| Dielectric Strength, in oil, 1.6 mm | 19 | kV/mm | ASTM D149 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 80 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.07 | % | |
| Minimum Moisture Content | 0.02 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Nozzle Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 275 - 305 | °C | |
| Middle - Zone 2 Temperature | 270 - 305 | °C | |
| Rear - Zone 1 Temperature | 265 - 305 | °C | |
| Mold Temperature | 75 - 120 | °C | |
| Back Pressure | 0.3 - 1.4 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 50 | % | |
| Vent Depth | 0.013 - 0.038 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Nominal Stress, yld, Type I, 5 mm/min | 151 | MPa | ASTM D638 |
| Nominal Strain, brk, 5 mm/min | 158 | % | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 248 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 8580 | MPa | ASTM D790 |
| Hardness, Rockwell R | 120 | - | ASTM D785 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.33 | - | ASTM D792 |
| Density | 1.328 | g/cm³ | ASTM D792 |
| Moisture Absorption, (50% RH, Equilibrium) | 1 | % | ASTM D570 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.5 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.3 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.65 - 0.85 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 248 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 254 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 240 | °C | ASTM D648 |
| CTE, -20°C to 150°C, flow | 0 - 0 | 1/°C | ASTM E831 |
Your PDF is downloading. Please wait.