NORYL GTX™ Resin GTX850

NORYL GTX850 resin is a 50% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 15.2 GPa), excellent chemical resistance, and high heat resistance. Target application of GTX850 is a wide variety of automotive under-the-hood, water management and consumer electronics structural applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
High stiffness/Strength
High temperature resistance
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood
Water Management

Applications

Possible usage of material

Electronics
Meter Water
Pump
Underhood
Structural
biw
body in white
protection
energy absorption
ecoat
metal plastic hybrid

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	128	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1200	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	12.5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 105	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.07	%
Minimum Moisture Content	0.02	%
Melt Temperature	280 - 305	°C
Nozzle Temperature	280 - 305	°C
Front - Zone 3 Temperature	275 - 305	°C
Middle - Zone 2 Temperature	270 - 305	°C
Rear - Zone 1 Temperature	265 - 305	°C
Mold Temperature	75 - 120	°C
Back Pressure	0.3 - 1.4	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%
Vent Depth	0.013 - 0.038	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	232	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.6	%	ASTM D638
Tensile Modulus, 5 mm/min	17500	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	370	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	15200	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	226	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3.3	%	ISO 527
Tensile Modulus, 1 mm/min	17000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	365	MPa	ISO 178
Flexural Modulus, 2 mm/min	14800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.575	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.31	%	ISO 62-1
Mold Shrinkage, flow	0.3 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.35 - 0.45	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	251	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	250	°C	ISO 75/Af

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards