ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
NORYL GTX GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 60 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 17 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Minimum Moisture Content | 0.02 | % | |
Melt Temperature | 280 - 305 | °C | |
Nozzle Temperature | 280 - 305 | °C | |
Front - Zone 3 Temperature | 275 - 305 | °C | |
Middle - Zone 2 Temperature | 270 - 305 | °C | |
Rear - Zone 1 Temperature | 265 - 305 | °C | |
Mold Temperature | 75 - 120 | °C | |
Back Pressure | 0.3 - 1.4 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 50 | % | |
Vent Depth | 0.013 - 0.038 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7000 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 200 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 200 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 6600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.26 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.26 - 0.3 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.72 - 0.85 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 8.6 | g/10 min | ASTM D1238 |
Density | 1.26 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 225 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 60 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 17 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Minimum Moisture Content | 0.02 | % | |
Melt Temperature | 280 - 305 | °C | |
Nozzle Temperature | 280 - 305 | °C | |
Front - Zone 3 Temperature | 275 - 305 | °C | |
Middle - Zone 2 Temperature | 270 - 305 | °C | |
Rear - Zone 1 Temperature | 265 - 305 | °C | |
Mold Temperature | 75 - 120 | °C | |
Back Pressure | 0.3 - 1.4 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 50 | % | |
Vent Depth | 0.013 - 0.038 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7000 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 200 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 200 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 6600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.26 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.26 - 0.3 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.72 - 0.85 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 8.6 | g/10 min | ASTM D1238 |
Density | 1.26 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 225 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 60 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 17 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Minimum Moisture Content | 0.02 | % | |
Melt Temperature | 280 - 305 | °C | |
Nozzle Temperature | 280 - 305 | °C | |
Front - Zone 3 Temperature | 275 - 305 | °C | |
Middle - Zone 2 Temperature | 270 - 305 | °C | |
Rear - Zone 1 Temperature | 265 - 305 | °C | |
Mold Temperature | 75 - 120 | °C | |
Back Pressure | 0.3 - 1.4 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 50 | % | |
Vent Depth | 0.013 - 0.038 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7000 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 200 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.1 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 200 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 6600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.26 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.26 - 0.3 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.72 - 0.85 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 8.6 | g/10 min | ASTM D1238 |
Density | 1.26 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 225 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | - | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | - | - | - |
UL Recognized, 94HB Flame Class Rating | - | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | - | J/m | ASTM D256 |
Izod Impact, notched, -30°C | - | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | - | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | - | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | - | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | - | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | - | °C | |
Drying Time | - | Hrs | |
Drying Time (Cumulative) | - | Hrs | |
Maximum Moisture Content | - | % | |
Minimum Moisture Content | - | % | |
Melt Temperature | - | °C | |
Nozzle Temperature | - | °C | |
Front - Zone 3 Temperature | - | °C | |
Middle - Zone 2 Temperature | - | °C | |
Rear - Zone 1 Temperature | - | °C | |
Mold Temperature | - | °C | |
Back Pressure | - | MPa | |
Screw Speed | - | rpm | |
Shot to Cylinder Size | - | % | |
Vent Depth | - | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | - | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | - | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | - | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | - | % | ASTM D638 |
Tensile Modulus, 5 mm/min | - | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | - | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | - | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | - | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | - | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | - | % | ISO 527 |
Tensile Strain, break, 5 mm/min | - | % | ISO 527 |
Tensile Modulus, 1 mm/min | - | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | - | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | - | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | - | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | - | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | - | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | - | g/10 min | ASTM D1238 |
Density | - | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | - | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | - | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | - | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | - | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | - | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | - | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | - | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | - | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | - | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | - | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | - | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | - | °C | ISO 75/Bf |