NORYL GTX™ Resin GTX902BIO3

Sustainable Grade

NORYL GTX902BIO3 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA) with bio-based content. This injection moldable grade exhibits excellent chemical resistance and excellent paintability. NORYL GTX902BIO3 resin is targeted for automotive wheel cover applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Sustainable (bio-based offerings)

Industry

Material previously used in

Automotive Exteriors
Heavy Truck
Personal Recreation
Recreational/Specialty Vehicles

Applications

Possible usage of material

Mobile Phone
Commercial Appliance
Electrical
Electronic Components
Energy Management
Houseware & appliances

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	18	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	19	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	220	J/m	ASTM D256
Izod Impact, notched, -30°C	117	J/m	ASTM D256
Izod Impact, notched, -40°C	53	J/m	ASTM D256
Izod Impact, unnotched, 23°C	3204	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	3204	J/m	ASTM D4812
Izod Impact, unnotched, -40°C	3204	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	46	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, -30°C	36	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 105	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.07	%
Minimum Moisture Content	0.02	%
Melt Temperature	275 - 300	°C
Rear - Zone 1 Temperature	260 - 300	°C
Middle - Zone 2 Temperature	265 - 300	°C
Front - Zone 3 Temperature	270 - 300	°C
Nozzle Temperature	275 - 300	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.3 - 1.4	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%
Vent Depth	0.013 - 0.038	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	58	MPa	ISO 527
Tensile Stress, break, 50 mm/min	54	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	9	%	ISO 527
Tensile Strain, break, 50 mm/min	46	%	ISO 527
Tensile Modulus, 1 mm/min	2154	MPa	ISO 527
Flexural Modulus, 2 mm/min	2227	MPa	ISO 178
Flexural Strength, 2 mm/min	91	MPa	ISO 178
Tensile Modulus, 50 mm/min	2173	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	45	%	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	11	%	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	58	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2120	MPa	ASTM D790
Flexural Strength, 2.6 mm/min, 100 mm span	89	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	2240	MPa	ASTM D790
Hardness, Rockwell R	118	-	ASTM D785
Taber Abrasion, CS-17, 1 kg	19	mg/1000cy	ASTM D1044

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.09	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.2	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.57	%	ISO 62-4
Water Absorption, (23°C/saturated)	2.02	%	ISO 62-1
Water Absorption, (23°C/24hrs)	0.73	%	ISO 62-1
Mold Shrink, flow, annealed 130C 1hr	1.1 - 1.5	%	ASTM D955
Mold Shrinkage, flow, 3.2 mm	0.9 - 1.2	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.8 - 1.1	%	SABIC method
Melt Volume Rate, MVR at 280°C/2.16 kg	5.4	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 280°C/5.0 kg	12	cm³/10 min	ISO 1133
Specific Gravity	1.08	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.73	%	ASTM D570
Water Absorption, (23°C/Saturated)	2.81	%	ASTM D570
Melt Flow Rate, 280°C/2.16 kgf	3.4	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	113	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	154	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	155	°C	ASTM D648
Vicat Softening Temp, Rate B/50	166	°C	ISO 306
Vicat Softening Temp, Rate A/50	235	°C	ISO 306
Vicat Softening Temp, Rate B/50	200	°C	ASTM D1525
Vicat Softening Temp, Rate A/50	232	°C	ASTM D1525
CTE, 23°C to 60°C, flow	9.3E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, xflow	9.3E-05	1/°C	ASTM E831
CTE, -20°C to 150°C, flow	9.0E-05	1/°C	ASTM E831
CTE, -20°C to 150°C, xflow	9.3E-05	1/°C	ASTM E831
Relative Temp Index, Elec	50	°C	UL 746B
Relative Temp Index, Mech w/impact	50	°C	UL 746B
Relative Temp Index, Mech w/o impact	50	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES