NORYL GTX™ Resin GTX910C

NORYL GTX910C resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). NORYL GTX910C resin exhibits excellent chemical resistance and is targeted for automotive applications such as exterior automotive applications such as wheel covers and wheel trim.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Creep resistant
Dimensional stability
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors

Applications

Possible usage of material

Automotive

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	621	J/m	ASTM D256
Izod Impact, notched, -30°C	166	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	16	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	14	kJ/m²	ISO 179/1eA
Instrumented Dart Impact Total Energy, 23°C	50	J	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	45	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 305	°C
Nozzle Temperature	280 - 305	°C
Front - Zone 3 Temperature	280 - 305	°C
Middle - Zone 2 Temperature	270 - 300	°C
Rear - Zone 1 Temperature	260 - 290	°C
Mold Temperature	20 - 80	°C
Back Pressure	0.4 - 0.6	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%
Vent Depth	0.013 - 0.038	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	48	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	46	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	22	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	63	%	ASTM D638
Tensile Modulus, 50 mm/min	1992	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	67	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1530	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	47	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	9	%	ISO 527
Tensile Strain, break, 50 mm/min	69	%	ISO 527
Tensile Modulus, 1 mm/min	1955	MPa	ISO 527
Flexural Strength, 2 mm/min	63	MPa	ISO 178
Flexural Modulus, 2 mm/min	1538	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.09	-	ASTM D792
Melt Flow Rate, 280°C/2.16 kgf	15	g/10 min	ASTM D1238
Melt Flow Rate, 280°C/5.0 kgf	50	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/2.16 kg	19	cm³/10 min	ISO 1133
Water Absorption, 23°C/24hrs	0.81	%	SABIC method
Mold Shrinkage, flow	0.98 - 1.01	%	SABIC method
Mold Shrinkage, xflow	1.01 - 1.04	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	158	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	86	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	159	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	75	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	8.6E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.6E-05	1/°C	ASTM E831
Vicat Softening Temp, Rate B/50	172	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	172	°C	ASTM D1525
Vicat Softening Temp, Rate A/50	208	°C	ISO 306
Vicat Softening Temp, Rate A/120	206	°C	ISO 306

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	621	J/m	ASTM D256
Izod Impact, notched, -30°C	166	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	16	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	14	kJ/m²	ISO 179/1eA
Instrumented Dart Impact Total Energy, 23°C	50	J	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	45	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 305	°C
Nozzle Temperature	280 - 305	°C
Front - Zone 3 Temperature	280 - 305	°C
Middle - Zone 2 Temperature	270 - 300	°C
Rear - Zone 1 Temperature	260 - 290	°C
Mold Temperature	20 - 80	°C
Back Pressure	0.4 - 0.6	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%
Vent Depth	0.013 - 0.038	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	48	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	46	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	22	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	63	%	ASTM D638
Tensile Modulus, 50 mm/min	1992	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	67	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1530	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	47	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	9	%	ISO 527
Tensile Strain, break, 50 mm/min	69	%	ISO 527
Tensile Modulus, 1 mm/min	1955	MPa	ISO 527
Flexural Strength, 2 mm/min	63	MPa	ISO 178
Flexural Modulus, 2 mm/min	1538	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.09	-	ASTM D792
Melt Flow Rate, 280°C/2.16 kgf	15	g/10 min	ASTM D1238
Melt Flow Rate, 280°C/5.0 kgf	50	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/2.16 kg	19	cm³/10 min	ISO 1133
Water Absorption, 23°C/24hrs	0.81	%	SABIC method
Mold Shrinkage, flow	0.98 - 1.01	%	SABIC method
Mold Shrinkage, xflow	1.01 - 1.04	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	158	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	86	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	159	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	75	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	8.6E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.6E-05	1/°C	ASTM E831
Vicat Softening Temp, Rate B/50	172	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	172	°C	ASTM D1525
Vicat Softening Temp, Rate A/50	208	°C	ISO 306
Vicat Softening Temp, Rate A/120	206	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

NORYL GTX™ Resin GTX910C

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents