NORYL GTX942 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high melt flow, excellent chemical resistance and paintability. NORYL GTX942 resin was designed for large part / thin wall applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 265 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 117 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 46 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 22 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 23 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.07 | % | |
| Minimum Moisture Content | 0.02 | % | |
| Melt Temperature | 275 - 300 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Front - Zone 3 Temperature | 270 - 300 | °C | |
| Middle - Zone 2 Temperature | 265 - 300 | °C | |
| Rear - Zone 1 Temperature | 260 - 300 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.3 - 1.4 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 50 | % | |
| Vent Depth | 0.013 - 0.038 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 43.9 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2440 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 87 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2260 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7.1 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 58.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2580 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2220 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.09 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 1.13 - 1.26 | % | SABIC method |
| Melt Flow Rate, 280°C/5.0 kgf | 18.5 | g/10 min | ASTM D1238 |
| Density | 1.09 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 1.01 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.52 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 17 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 171 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 160 | °C | ASTM D648 |
| CTE, -40°C to 95°C, flow | 9.E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 95°C, xflow | 7.E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 80°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 169 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 169 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 154 | °C | ISO 75/Bf |