NORYL GTX™ Resin GTX944

NORYL GTX944 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance along with improved processability and increased impact performance. NORYL GTX944 resin may be an excellent candidate for Firefighter Helmet applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Building Component
Electronic Components

Applications

Possible usage of material

Building Element
Defense
Electronic Components
Enclosures
Exterior
Head Protection
Heavy Vehicles
automotive exterior
automotive ev
automotive aftermarket

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	2.2E+13	Ω.cm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	20	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.072	-	IEC 60250
Dissipation Factor, 1 MHz	0.024	-	IEC 60250
Comparative Tracking Index	600	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.5	-	IEC 60250

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94HB Flame Class Rating	1.6	mm	UL 94 by SABIC-IP
Oxygen Index (LOI)	21	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	680	J/m	ASTM D256
Izod Impact, notched, -30°C	280	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	55	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	55	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -20°C*	25	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	25	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	25	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.07	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	45	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 50 mm/min	1900	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	75	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1950	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.5	%	ISO 527
Tensile Strain, break, 50 mm/min	50	%	ISO 527
Tensile Modulus, 1 mm/min	2000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	75	MPa	ISO 178
Flexural Modulus, 2 mm/min	1900	MPa	ISO 178
Ball Indentation Hardness, H358/30	75	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Mold Shrinkage on Tensile Bar, flow	1.4 - 1.8	%	SABIC method
Mold Shrinkage, flow, 3.2 mm	1.4 - 1.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1.1 - 1.4	%	SABIC method
Melt Flow Rate, 280°C/5.0 kgf	12.5	g/10 min	ASTM D1238
Density	1.07	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	3.5	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	1.2	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	12	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	180	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	185	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.E-04	1/°C	ASTM E831
Thermal Conductivity	0.24	W/m-°C	ISO 8302
CTE, 23°C to 60°C, flow	9.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	240	°C	ISO 306
Vicat Softening Temp, Rate B/50	180	°C	ISO 306
Vicat Softening Temp, Rate B/120	185	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	175	°C	ISO 75/Be

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	2.2E+13	Ω.cm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	20	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.072	-	IEC 60250
Dissipation Factor, 1 MHz	0.024	-	IEC 60250
Comparative Tracking Index	600	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.5	-	IEC 60250

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94HB Flame Class Rating	1.6	mm	UL 94 by SABIC-IP
Oxygen Index (LOI)	21	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	680	J/m	ASTM D256
Izod Impact, notched, -30°C	280	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	55	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	55	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -20°C*	25	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	25	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	25	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.07	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	45	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 50 mm/min	1900	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	75	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1950	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.5	%	ISO 527
Tensile Strain, break, 50 mm/min	50	%	ISO 527
Tensile Modulus, 1 mm/min	2000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	75	MPa	ISO 178
Flexural Modulus, 2 mm/min	1900	MPa	ISO 178
Ball Indentation Hardness, H358/30	75	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Mold Shrinkage on Tensile Bar, flow	1.4 - 1.8	%	SABIC method
Mold Shrinkage, flow, 3.2 mm	1.4 - 1.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1.1 - 1.4	%	SABIC method
Melt Flow Rate, 280°C/5.0 kgf	12.5	g/10 min	ASTM D1238
Density	1.07	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	3.5	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	1.2	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	12	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	180	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	185	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.E-04	1/°C	ASTM E831
Thermal Conductivity	0.24	W/m-°C	ISO 8302
CTE, 23°C to 60°C, flow	9.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	240	°C	ISO 306
Vicat Softening Temp, Rate B/50	180	°C	ISO 306
Vicat Softening Temp, Rate B/120	185	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	175	°C	ISO 75/Be

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	2.2E+13	Ω.cm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	20	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.072	-	IEC 60250
Dissipation Factor, 1 MHz	0.024	-	IEC 60250
Comparative Tracking Index	600	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.5	-	IEC 60250

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94HB Flame Class Rating	1.6	mm	UL 94 by SABIC-IP
Oxygen Index (LOI)	21	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	680	J/m	ASTM D256
Izod Impact, notched, -30°C	280	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	55	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	55	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -20°C*	25	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	25	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	25	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.07	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	45	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 50 mm/min	1900	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	75	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1950	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.5	%	ISO 527
Tensile Strain, break, 50 mm/min	50	%	ISO 527
Tensile Modulus, 1 mm/min	2000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	75	MPa	ISO 178
Flexural Modulus, 2 mm/min	1900	MPa	ISO 178
Ball Indentation Hardness, H358/30	75	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Mold Shrinkage on Tensile Bar, flow	1.4 - 1.8	%	SABIC method
Mold Shrinkage, flow, 3.2 mm	1.4 - 1.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1.1 - 1.4	%	SABIC method
Melt Flow Rate, 280°C/5.0 kgf	12.5	g/10 min	ASTM D1238
Density	1.07	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	3.5	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	1.2	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	12	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	180	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	185	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.E-04	1/°C	ASTM E831
Thermal Conductivity	0.24	W/m-°C	ISO 8302
CTE, 23°C to 60°C, flow	9.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	240	°C	ISO 306
Vicat Softening Temp, Rate B/50	180	°C	ISO 306
Vicat Softening Temp, Rate B/120	185	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	175	°C	ISO 75/Be

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

NORYL GTX™ Resin GTX944

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents

Technical Data Sheets

Register for High value Multi-Point Data