NORYL GTX™ Resin GTX9500

NORYL GTX9500 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This resin exhibits a good balance of high melt flow and low water absorption. Added features include excellent chemical resistance, high heat resistance, and dimensional stability. NORYL GTX9500 is an excellent candidate for various applications in the automotive and electronics industries.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Creep resistant
Good Processability
High stiffness/Strength
Hydrolytic Stability
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors
Automotive Under the Hood
Electrical
Recreational/Specialty Vehicles

Applications

Possible usage of material

Auto Aftermarket
Auto Electrical
Circuit Protection
Electronic Components
Recreational Vehicle

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Strength, in oil, 1.6 mm	25.9	kV/mm	ASTM D149
Dissipation Factor, 1 MHz	0.01	-	ASTM D150

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	41	J/m	ASTM D256
Izod Impact, notched, -30°C	28	J/m	ASTM D256
Izod Impact, unnotched, 23°C	800	J/m	ASTM D4812
Instrumented Impact Total Energy, 23°C	11	J	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	4	J	ASTM D3763
*Charpy Impact, notched, 23°C, 80104mm, Cut*	7	kJ/m²	ISO 179/1eA
*Charpy Impact, notched, -30°C, 80104mm, Cut*	6	kJ/m²	ISO 179/1eA
Charpy Impact, unnotched, 23°C	51	kJ/m²	ISO 179/2C
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	64	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 105	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.07	%
Minimum Moisture Content	0.02	%
Melt Temperature	270 - 295	°C
Nozzle Temperature	270 - 295	°C
Front - Zone 3 Temperature	265 - 295	°C
Middle - Zone 2 Temperature	260 - 295	°C
Rear - Zone 1 Temperature	255 - 295	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.3 - 1.4	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%
Vent Depth	0.013 - 0.038	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	61	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	57	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	6	%	ASTM D638
Tensile Modulus, 50 mm/min	2142	MPa	ASTM D638
Tensile Stress, yield, 50 mm/min	60	MPa	ISO 527
Tensile Stress, break, 50 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	9	%	ISO 527
Tensile Modulus, 1 mm/min	2355	MPa	ISO 527
Flexural Stress, yld, 1.3 mm/min, 50 mm span	90	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2356.9	MPa	ASTM D790
Flexural Stress, yld, 2.6 mm/min, 100 mm span	66	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	1973	MPa	ASTM D790
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2305	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.10	-	ASTM D792
Mold Shrinkage, flow	1.771	%	SABIC method
Mold Shrinkage, xflow	1.885	%	SABIC method
Water Absorption, (23°C/48hrs)	0.68	%	ASTM D570
Moisture Absorption (23°C / 50% RH)	0.17	%	ISO 62
Melt Flow Rate, 280°C/2.16 kgf	28	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	123	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	65	°C	ASTM D648
Vicat Softening Temp, Rate B/50	152	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	155.4	°C	ASTM D1525
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	135.5	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	92.5	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
Vicat Softening Temp, Rate B/120	154	°C	ISO 306
CTE, -40°C to 40°C, flow	7.17E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.55E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, flow	8.62E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.02E-04	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES