NORYL GTX964 resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance and high melt flow for optimized processability. NORYL GTX964 resin is impact modified and designed for automotive exterior thin wall, large parts such as body panels.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2 - 3 | Hrs | |
| Maximum Moisture Content | 0.07 | % | |
| Melt Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Front - Zone 3 Temperature | 290 - 320 | °C | |
| Middle - Zone 2 Temperature | 280 - 300 | °C | |
| Rear - Zone 1 Temperature | 260 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 80 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 80 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 1.4 - 1.8 | % | SABIC method |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 3.5 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 1.19 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/2.16 kg | 7 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 240 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Be |