NORYL GTX964W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA) that exhibits very high impact resistance and high flow. This injection moldable grade was designed for large parts, such as automotive body panels, and thin wall applications
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 528 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 41 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.07 | % | |
| Minimum Moisture Content | 0.02 | % | |
| Melt Temperature | 295 - 315 | °C | |
| Nozzle Temperature | 295 - 315 | °C | |
| Front - Zone 3 Temperature | 290 - 315 | °C | |
| Middle - Zone 2 Temperature | 280 - 315 | °C | |
| Rear - Zone 1 Temperature | 275 - 315 | °C | |
| Mold Temperature | 75 - 120 | °C | |
| Back Pressure | 0.3 - 1.4 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 50 | % | |
| Vent Depth | 0.013 - 0.038 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 44 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 56 | % | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 73 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 1830 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.08 | - | ASTM D792 |
| Water Absorption, (23°C/Saturated) | 3.5 | % | ASTM D570 |
| Moisture Absorption, (50% RH, Equilibrium) | 1.19 | % | ASTM D570 |
| Mold Shrinkage, flow | 1.5 | % | SABIC method |
| Mold Shrinkage, xflow | 1.3 | % | SABIC method |
| Melt Volume Rate, MVR at 280°C/2.16 kg | 7 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 6.4 mm, unannealed | 185 | °C | ASTM D648 |
| Thermal Conductivity | 0.23 | W/m-°C | ASTM C177 |
| Vicat Softening Temp, Rate A/50 | 240 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Be |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.