ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
NORYL GTX974 resin is a conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for in- or on-line primer-less electrostatic painting. NORYL GTX974 resin exhibits high impact resistance and is an excellent candidate for automotive painted applications such as body panels and fenders.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 180 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 50 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 18 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 120 | °C | |
Drying Time | 2 - 3 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Melt Temperature | 290 - 320 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 290 - 320 | °C | |
Middle - Zone 2 Temperature | 280 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 100 - 120 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2050 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 30 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.08 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 1.3 - 1.6 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 1.1 - 1.4 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.08 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4.2 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 1.2 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 180 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E831 |
CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 230 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Be |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 180 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 50 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 18 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 120 | °C | |
Drying Time | 2 - 3 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Melt Temperature | 290 - 320 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 290 - 320 | °C | |
Middle - Zone 2 Temperature | 280 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 100 - 120 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2050 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 30 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.08 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 1.3 - 1.6 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 1.1 - 1.4 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.08 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4.2 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 1.2 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 180 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E831 |
CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 230 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Be |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+03 - 1.E+04 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 180 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 50 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 18 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 120 | °C | |
Drying Time | 2 - 3 | Hrs | |
Maximum Moisture Content | 0.07 | % | |
Melt Temperature | 290 - 320 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 290 - 320 | °C | |
Middle - Zone 2 Temperature | 280 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 100 - 120 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 50 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2050 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 30 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.08 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 1.3 - 1.6 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 1.1 - 1.4 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.08 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 4.2 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 1.2 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 180 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E831 |
CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 230 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Be |