NORYL GTX™ Resin GTX9811

NORYL GTX9811 resin is a conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized to allow for in- or on-line primer-less electrostatic and powder coat painting. NORYL GTX9811 resin exhibits high impact strength, excellent flow and good dimension stability. This product is targeted for automotive painted applications such as body panels, tank flaps and EV service flaps. See NORYL GTX9810 resin for improved dimension stability version.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dimensional stability
Electrically Conductive
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors

Applications

Possible usage of material

Automotive

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	5.0E+02 - 1.0E+04	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	142	J/m	ASTM D256
Izod Impact, notched, -30°C	60	J/m	ASTM D256
Izod Impact, unnotched, 23°C	810	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	830	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	68	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	82	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	17	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	51	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.07	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	100 - 120	°C
Back Pressure	0.4 - 1.0	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 50	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	66	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	50	%	ASTM D638
Tensile Modulus, 5 mm/min	2650	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	94	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2350	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	66	MPa	ISO 527
Tensile Stress, break, 50 mm/min	59	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	53	%	ISO 527
Tensile Modulus, 1 mm/min	2860	MPa	ISO 527
Flexural Strength, 2 mm/min	92	MPa	ISO 178
Flexural Modulus, 2 mm/min	2400	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.10	-	ASTM D792
Density	1.10	g/cm³	ISO 1183
Melt Flow Rate, 280°C/5.0 kgf	23	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/5.0 kg	21	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.51	%	ISO 62-1
Water Absorption, (23°C/saturated)	3.61	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.12	%	ISO 62-4
Mold Shrinkage, flow	1.5 - 1.7	%	SABIC method
Mold Shrinkage, xflow	1.5 - 1.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	206	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	191	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	116	°C	ISO 75/Af
CTE, -40°C to 60°C, flow	7.7E-05	1/°C	ASTM E831
CTE, -40°C to 60°C, xflow	7.6E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, flow	8.0E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	8.1E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	204	°C	ISO 306
Vicat Softening Temp, Rate B/120	207	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES