NORYL GTX™ Resin GTX985

NORYL GTX985 resin is a conductive, 18% mineral reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade combines high stiffness, excellent chemical resistance, and high heat resistance. NORYL GTX985 is conductive for primerless electrostatic painting and is an excellent candidate for automotive exterior trim applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PA (PPE+Nylon)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Chemical Resistance
Dimensional stability
Electrically Conductive
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors

Applications

Possible usage of material

Exterior Trim
Fuel Handling

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	45	J/m	ASTM D256
Izod Impact, notched, -30°C	40	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	10	J	ASTM D3763
*Izod Impact, unnotched 80103 +23°C*	60	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	4	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	4	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 110	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 300	°C
Nozzle Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	100 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	65	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	7	%	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	110	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4200	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	65	MPa	ISO 527
Tensile Stress, break, 5 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4	%	ISO 527
Tensile Strain, break, 5 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	4400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	105	MPa	ISO 178
Flexural Modulus, 2 mm/min	4350	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 3.2 mm	0.8 - 1.2	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.8 - 1.2	%	SABIC method
Specific Gravity	1.25	-	ASTM D792
Melt Flow Rate, 280°C/5.0 kgf	16	g/10 min	ASTM D1238
Density	1.25	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	1.1	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	15	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	195	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	200	°C	ASTM D648
CTE, 23°C to 60°C, flow	6.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	195	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Bf

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	45	J/m	ASTM D256
Izod Impact, notched, -30°C	40	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	10	J	ASTM D3763
*Izod Impact, unnotched 80103 +23°C*	60	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	4	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	4	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 110	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 300	°C
Nozzle Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	100 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	65	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	7	%	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	110	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4200	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	65	MPa	ISO 527
Tensile Stress, break, 5 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4	%	ISO 527
Tensile Strain, break, 5 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	4400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	105	MPa	ISO 178
Flexural Modulus, 2 mm/min	4350	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.25	-	ASTM D792
Melt Flow Rate, 280°C/5.0 kgf	16	g/10 min	ASTM D1238
Density	1.25	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	1.1	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	15	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 3.2 mm	0.8 - 1.2	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.8 - 1.2	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	195	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	200	°C	ASTM D648
CTE, 23°C to 60°C, flow	6.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	195	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Bf

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+03 - 1.E+04	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	45	J/m	ASTM D256
Izod Impact, notched, -30°C	40	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	10	J	ASTM D3763
*Izod Impact, unnotched 80103 +23°C*	60	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	55	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	4	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	4	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 110	°C
Drying Time	2 - 3	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 300	°C
Nozzle Temperature	270 - 290	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	270 - 290	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	100 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	65	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	7	%	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	110	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	4200	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	65	MPa	ISO 527
Tensile Stress, break, 5 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4	%	ISO 527
Tensile Strain, break, 5 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	4400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	105	MPa	ISO 178
Flexural Modulus, 2 mm/min	4350	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.25	-	ASTM D792
Melt Flow Rate, 280°C/5.0 kgf	16	g/10 min	ASTM D1238
Density	1.25	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	1.1	%	ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg	15	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 3.2 mm	0.8 - 1.2	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.8 - 1.2	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	195	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	200	°C	ASTM D648
CTE, 23°C to 60°C, flow	6.E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	195	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Bf

THIS SITE USES COOKIES

NORYL GTX™ Resin GTX985

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

NORYL GTX™ Resin GTX985

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards