NORYL GTX™ Resin LMX310

NORYL GTX LMX310 resin is a low CO2 footprint, conductive, non-reinforced alloy of Polyphenylene Ether (PPE) + Polybutylene Terephthalate (PBT). This injection moldable grade is optimized for primer-less electrostatic painting. NORYL GTX LMX310 resin exhibits high heat performance, low moisture uptake and low warpage. This material is a suitable material for automotive applications such as body panels, service flaps, fenders, trunk lid, and exterior trim.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PBT (PPE+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Low Moisture Absorption
Low Warpage

Industry

Material previously used in

Automotive Exteriors

Applications

Possible usage of material

Door Handle
Horizontal Body Panel
Vertical Body Panel

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+03 - 1.E+04	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	132	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 -30°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 -30°C*	35	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	100	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	46	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	7	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	112	J/m	ASTM D256
Izod Impact, notched, -30°C	106	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	12	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.07	%
Hopper Temperature	60 - 80	°C
Melt Temperature	260 - 280	°C
Rear - Zone 1 Temperature	230 - 240	°C
Middle - Zone 2 Temperature	250 - 260	°C
Front - Zone 3 Temperature	270 - 280	°C
Nozzle Temperature	270 - 280	°C
Mold Temperature	90 - 100	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2110	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	49	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Nominal Strain, break, 50 mm/min	20	%	ISO 527
Flexural Modulus, 2 mm/min	2090	MPa	ISO 178
Flexural Strength, 2 mm/min	75	MPa	ISO 178
Tensile Modulus, 50 mm/min	2110	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	46	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	20	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	2210	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.19	g/cm³	ISO 1183
Specific Gravity	1.19	-	ASTM D792
Melt Volume Rate, MVR at 260°C/5.0 kg	15	cm³/10 min	ISO 1133
Melt Flow Rate, 260°C/5.0 kgf	17	g/10 min	ASTM D1238
Moisture Absorption, (23°C/50% RH/24hrs)	0	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.03	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.10	%	ISO 62-1
Water Absorption, (23°C/saturated)	0.27	%	ISO 62-1
Mold Shrinkage, flow	2.10 - 2.20	%	SABIC method
Mold Shrinkage, xflow	2.05 - 2.15	%	SABIC method
Mold Shrinkage, flow	1.65 - 1.85	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	102	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	164	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2 mm	106	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm	178	°C	ASTM D648
Vicat Softening Temp, Rate B/50	168	°C	ISO 306
Vicat Softening Temp, Rate B/120	169	°C	ISO 306
Vicat Softening Temp, Rate B/50	168	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	169	°C	ASTM D1525
CTE, 23°C to 60°C, flow	12.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	12.6E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, flow	12.5E-05	1/°C	ASTM E831
CTE, 23°C to 60°C, xflow	12.6E-05	1/°C	ASTM E831

THIS SITE USES COOKIES

NORYL GTX™ Resin LMX310

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

NORYL GTX™ Resin LMX310

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Related Documents

Technical Data Sheets

Register for High value Multi-Point Data