NORYL 6850H resin concentrate is an non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This material is in granule form and is optimized for blending with polystyrene resins. NORYL 6850H resin may be an excellent candidate in microwavable food packaging applications. This product is not certified per food contact regulations in US + EUR. Certification would be dependent on end-part testing.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 18 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 51 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2340 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 97 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2380 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.25 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 20 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 280°C, 1500 sec-1 | 140 | Pa-s | ISO 11443 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 141 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 147 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Af |