FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | 1 | mm | UL 94 |
Glow Wire Flammability Index 650°C, passes at | 3 | mm | IEC 60695-2-12 |
NORYL PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. NORYL PPX830 is an opaque material available in limited colors only.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | 1 | mm | UL 94 |
Glow Wire Flammability Index 650°C, passes at | 3 | mm | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 95 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 10 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 36 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 65 - 75 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 300 | °C | |
Nozzle Temperature | 260 - 300 | °C | |
Front - Zone 3 Temperature | 255 - 290 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 245 - 290 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 40 - 65 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 101 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 144 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7700 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 141 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.25 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 6 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 2.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 1.3E-04 | 1/°C | ASTM E831 |
CTE, -30°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
CTE, -30°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/120 | 150 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 168 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 153 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | 1 | mm | UL 94 |
Glow Wire Flammability Index 650°C, passes at | 3 | mm | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 95 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 10 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 36 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 65 - 75 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 300 | °C | |
Nozzle Temperature | 260 - 300 | °C | |
Front - Zone 3 Temperature | 255 - 290 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 245 - 290 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 40 - 65 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 101 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 144 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7700 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 141 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.25 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 6 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 2.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 1.3E-04 | 1/°C | ASTM E831 |
CTE, -30°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
CTE, -30°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/120 | 150 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 168 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 153 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94HB Flame Class Rating | 1 | mm | UL 94 |
Glow Wire Flammability Index 650°C, passes at | 3 | mm | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 650 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 95 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 10 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | 42 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 36 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 65 - 75 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 300 | °C | |
Nozzle Temperature | 260 - 300 | °C | |
Front - Zone 3 Temperature | 255 - 290 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 245 - 290 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 40 - 65 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 101 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 101 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 7600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 144 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 6600 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 98 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 7700 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 141 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.25 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 6 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 2.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 1.3E-04 | 1/°C | ASTM E831 |
CTE, -30°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 |
CTE, -30°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/120 | 150 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 168 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 153 | °C | ISO 75/Af |