NORYL 141E compound is based on Polyphenylene Ether (PPE) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+04 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 59 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 270 - 310 | °C | |
| Nozzle Temperature | 265 - 305 | °C | |
| Front - Zone 3 Temperature | 270 - 310 | °C | |
| Middle - Zone 2 Temperature | 260 - 300 | °C | |
| Rear - Zone 1 Temperature | 250 - 290 | °C | |
| Mold Temperature | 70 - 110 | °C | |
| Back pressure (Plastic Pressure) | 5 - 10 | MPa | |
| Screw speed (Circumferential speed) | 0.1 - 0.2 | m/s | |
| Shot to Cylinder Size | 30 - 70 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 59 | MPa | SABIC - Japan Method |
| Tensile Strain, break | 7 | % | SABIC - Japan Method |
| Flexural Stress | 88 | MPa | ASTM D790 |
| Flexural Modulus | 2650 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.09 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.9 - 1 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 130 | °C | ASTM D648 |