IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 31 | J/m | ASTM D256 |
NORYL EFN4230S resin is a high heat, transparent, non-reinforced blend of polyphenylene ether (PPE) + general purpose polystyrene (GPPS). This FDA Food Contact compliant material may be an excellent candidate for food and industrial packaging applications. *See NORYL EFN4230 resin for NON FDA food compliant version
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 31 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 110 - 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 300 - 325 | °C | |
Nozzle Temperature | 300 - 325 | °C | |
Front - Zone 3 Temperature | 290 - 325 | °C | |
Middle - Zone 2 Temperature | 275 - 320 | °C | |
Rear - Zone 1 Temperature | 265 - 315 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 81 | MPa | SABIC - Japan Method |
Tensile Strain, break | 80 | % | SABIC - Japan Method |
Flexural Stress | 119 | MPa | ASTM D790 |
Flexural Modulus | 2800 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.08 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/5.0 kgf | 14.2 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 6.4 mm, unannealed | 147 | °C | ASTM D648 |
CTE, -30°C to 30°C | 6.0E-05 | 1/°C | TMA |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.