NORYL EK002 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade exhibits good surface appearance, high ductility, and good impact resistance along with low moisture absorption, creep resistance, dimensional stability, and hydrolytic stability. NORYL EK002 resin is an excellent candidate for a variety of applications.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 2.5 GHz | 2.59 | - | SABIC method |
| Dissipation Factor, 2.5 GHz | 0.0024 | - | SABIC method |
| Dielectric Constant, 5 GHz | 2.58 | - | SABIC method |
| Dissipation Factor, 5 GHz | 0.0024 | - | SABIC method |
| Dielectric Constant, 10 GHz | 2.58 | - | SABIC method |
| Dissipation Factor, 10 GHz | 0.0024 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 -30°C | 139 | kJ/m² | ISO 180/1U |
| Izod Impact, notched, 23°C | 214 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 112 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 2150 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 1550 | J/m | ASTM D4812 |
| Izod Impact, unnotched 80*10*4 +23°C | 214 | kJ/m² | ISO 180/1U |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280 - 310 | °C | |
| Rear - Zone 1 Temperature | 250 - 300 | °C | |
| Middle - Zone 2 Temperature | 260 - 305 | °C | |
| Front - Zone 3 Temperature | 270 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Mold Temperature | 75 - 105 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Shot to Cylinder Size | 30 - 70 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 53 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2490 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 2320 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min | 87 | MPa | ISO 178 |
| Tensile Strain, brk, Type I, 50 mm/min | 35 | % | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2300 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2460 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/10.0 kg | 12 | cm³/10 min | ISO 1133 |
| Specific Gravity | 1.06 | - | ASTM D792 |
| Melt Flow Rate, 250°C/10.0 kgf | 7 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| HDT, 1.82 MPa, 3.2mm, unannealed | 113 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 120 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |