FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
NORYL EM6100 is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This grade exhibits a balance of flow/heat/impact, dimensional stability, along with paint adhesion. NORYL EM6100 resin is targeted for the automotive interior market in applications such as HVAC housings and radio components. MS-DB424, WSBM4D844-A9, GMP.PPE.007.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 453 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 250 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 36 | J | ASTM D3763 |
Instrumented Dart Impact Energy @ peak, -30°C | 24 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, 23°C | 42 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy Impact, notched, 23°C | 33 | kJ/m² | ISO 179/2C |
Charpy Impact, notched, -30°C | 19 | kJ/m² | ISO 179/2C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 265 - 295 | °C | |
Nozzle Temperature | 265 - 295 | °C | |
Front - Zone 3 Temperature | 255 - 295 | °C | |
Middle - Zone 2 Temperature | 245 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 280 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % | |
Vent Depth | 0.038 - 0.051 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 40 | MPa | ASTM D638 |
Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
Tensile Strain, yield | 3 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 65 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D790 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 66 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 2000 | MPa | ASTM D790 |
Tensile Stress, yield | 42 | MPa | ISO 527 |
Tensile Stress, break | 40 | MPa | ISO 527 |
Tensile Strain, yield | 2.8 | % | ISO 527 |
Tensile Strain, break | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
Flexural Stress | 65 | MPa | ISO 178 |
Flexural Modulus | 2100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.05 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.2 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 115 | °C | ASTM D648 |
CTE, 0°C to 100°C, flow | 1.17E-04 | 1/°C | ASTM E831 |
Vicat Softening Temp, Rate B/50 | 119 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 453 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 250 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 36 | J | ASTM D3763 |
Instrumented Dart Impact Energy @ peak, -30°C | 24 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, 23°C | 42 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy Impact, notched, 23°C | 33 | kJ/m² | ISO 179/2C |
Charpy Impact, notched, -30°C | 19 | kJ/m² | ISO 179/2C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 265 - 295 | °C | |
Nozzle Temperature | 265 - 295 | °C | |
Front - Zone 3 Temperature | 255 - 295 | °C | |
Middle - Zone 2 Temperature | 245 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 280 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % | |
Vent Depth | 0.038 - 0.051 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 40 | MPa | ASTM D638 |
Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
Tensile Strain, yield | 3 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 65 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D790 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 66 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 2000 | MPa | ASTM D790 |
Tensile Stress, yield | 42 | MPa | ISO 527 |
Tensile Stress, break | 40 | MPa | ISO 527 |
Tensile Strain, yield | 2.8 | % | ISO 527 |
Tensile Strain, break | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
Flexural Stress | 65 | MPa | ISO 178 |
Flexural Modulus | 2100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.05 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.2 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 115 | °C | ASTM D648 |
CTE, 0°C to 100°C, flow | 1.17E-04 | 1/°C | ASTM E831 |
Vicat Softening Temp, Rate B/50 | 119 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 453 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 250 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 36 | J | ASTM D3763 |
Instrumented Dart Impact Energy @ peak, -30°C | 24 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, 23°C | 42 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy Impact, notched, 23°C | 33 | kJ/m² | ISO 179/2C |
Charpy Impact, notched, -30°C | 19 | kJ/m² | ISO 179/2C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 95 - 105 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 265 - 295 | °C | |
Nozzle Temperature | 265 - 295 | °C | |
Front - Zone 3 Temperature | 255 - 295 | °C | |
Middle - Zone 2 Temperature | 245 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 280 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % | |
Vent Depth | 0.038 - 0.051 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 40 | MPa | ASTM D638 |
Tensile Stress, yld, Type I, 50 mm/min | 43 | MPa | ASTM D638 |
Tensile Strain, yield | 3 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 65 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 67 | MPa | ASTM D790 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 66 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 2000 | MPa | ASTM D790 |
Tensile Stress, yield | 42 | MPa | ISO 527 |
Tensile Stress, break | 40 | MPa | ISO 527 |
Tensile Strain, yield | 2.8 | % | ISO 527 |
Tensile Strain, break | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
Flexural Stress | 65 | MPa | ISO 178 |
Flexural Modulus | 2100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.05 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.2 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 280°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 115 | °C | ASTM D648 |
CTE, 0°C to 100°C, flow | 1.17E-04 | 1/°C | ASTM E831 |
Vicat Softening Temp, Rate B/50 | 119 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 110 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |