NORYL™ Resin HFM3015P

NORYL HFM3015P resin is a 30% glass fiber and mineral reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm. NORYL HFM3015P resin exhibits exceptional dimensional stability, high stiffness and strength, strong electrical performance, very low moisture absorption, and hydrolytic stability. This material is an excellent candidate for internal structural parts such as chassis.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Amorphous
Dimensional stability
Flame Retardant
High stiffness/Strength
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Electronic Components
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Data Management
Document Handling

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	58	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 90	°C
Drying Time	2 - 4	Hrs
Melt Temperature	260 - 300	°C
Nozzle Temperature	260 - 300	°C
Front - Zone 3 Temperature	260 - 300	°C
Middle - Zone 2 Temperature	240 - 280	°C
Rear - Zone 1 Temperature	230 - 260	°C
Mold Temperature	60 - 90	°C
Back Pressure	0.5 - 1.2	MPa
Screw Speed	40 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	98	MPa	SABIC - Japan Method
Tensile Strain, break	4 - 6	%	SABIC - Japan Method
Flexural Stress	137	MPa	ASTM D790
Flexural Modulus	7640	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.32	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.06	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	0.25 - 0.3	%	SABIC method
Melt Flow Rate, 300°C/5.0 kgf	48.3	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 6.4 mm, unannealed	110	°C	ASTM D648
CTE, -30°C to 30°C	0.000025 - 0.000035	1/°C	TMA

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES