NORYL™ Resin IGN320

NORYL IGN320 resin is a 20% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade exhibits high heat resistance, high modulus, very low moisture absorption, and good dimensional stability. NORYL IGN320 resin is an excellent candidate for automotive applications such as ignition coils where heat and high modulus is required.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Americas

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood

Applications

Possible usage of material

Electrical
Engine Component
EV/HEV Invertor/Convertor
Ignition System
Sensor
ignition coil
pencil coil

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Strength, in oil, 1.6 mm	33.9	kV/mm	ASTM D149

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	512	J/m	ASTM D4812
Izod Impact, notched, 23°C	101	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	16	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	300 - 325	°C
Nozzle Temperature	300 - 325	°C
Front - Zone 3 Temperature	290 - 325	°C
Middle - Zone 2 Temperature	275 - 320	°C
Rear - Zone 1 Temperature	265 - 315	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 70	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	108	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	108	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Modulus, 5 mm/min	6260	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	170	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	5720	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Mold Shrinkage, flow, 3.2 mm	0.1 - 0.3	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.2 - 0.4	%	SABIC method
Melt Flow Rate, 300°C/5.0 kgf	12.8	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	175	°C	ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed	164	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	158	°C	ASTM D648

Register for High value Multi-Point Data