NORYL™ Resin LPN130HG

NORYL™ LPN130HG resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high gloss, low density, low outgassing and good dimensional stability performance. This extrusion and injection moldable grade has good processibility with density of 1.07 g/cm3, being capable for physical vapor deposition with good light distribution and high reflection rate. LPN130HG is targeted for automotive heads-up-display (HUD) reflector, headlamp reflector, bezel, light shielding and other high surface quality demanded components.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding
Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
High Flow
High gloss
High temperature resistance
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Lighting
Commercial Appliance
Electronic Components
Energy Management
Home Appliances
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Components
Automotive

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.2E+17	Ω	ASTM D257
Volume Resistivity	8.1E+16	Ω.cm	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	30	J/m	ASTM D256
Izod Impact, notched, -30°C	26	J/m	ASTM D256
Izod Impact, unnotched, 23°C	338	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	320	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	3.8	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	3.8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	19.9	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	20.7	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	2.7	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	2.7	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	24	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	26	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 6	Hrs
Melt Temperature	240 - 300	°C
Nozzle Temperature	240 - 300	°C
Front - Zone 3 Temperature	240 - 300	°C
Middle - Zone 2 Temperature	240 - 300	°C
Rear - Zone 1 Temperature	240 - 300	°C
Mold Temperature	90 - 155	°C
Screw Speed	20 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	78	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4.4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	6.8	%	ASTM D638
Tensile Modulus, 5 mm/min	3100	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	134	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3113	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	78	MPa	ISO 527
Tensile Stress, break, 5 mm/min	74	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.6	%	ISO 527
Tensile Strain, break, 5 mm/min	7.2	%	ISO 527
Tensile Modulus, 1 mm/min	3080	MPa	ISO 527
Flexural Strength, 2 mm/min	131	MPa	ISO 178
Flexural Modulus, 2 mm/min	3120	MPa	ISO 178

Optical properties

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Gloss (60°)	153	‰	ASTM D2457

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.07	-	ASTM D792
Density	1.07	g/cm³	ISO 1183
Melt Flow Rate, 280°C/5.0 kgf	18	g/10 min	ASTM D1238
Melt Flow Rate, 300°C/5.0 kgf	40	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/5.0 kg	16	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 300°C/5.0 kg	38	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.07	%	ISO 62-1
Mold Shrinkage, flow, 3.2 mm	0.76	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.92	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	132	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	119	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	132	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Af
CTE
– -40°C to 40°C, flow	7.8E-05	1/°C	ASTM E831
– -40°C to 40°C, xflow	7.7E-05	1/°C	ASTM E831
– -40°C to 85°C, flow	7.7E-05	1/°C	ASTM E831
– -40°C to 85°C, xflow	7.9E-05	1/°C	ASTM E831
– -40°C to 40°C, flow	7.4E-05	1/°C	ISO 11359-2
– -40°C to 40°C, xflow	7.5E-05	1/°C	ISO 11359-2
– -40°C to 85°C, flow	7.7E-05	1/°C	ISO 11359-2
– -40°C to 85°C, xflow	7.9E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	144	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	138	°C	ASTM D1525
Vicat Softening Temp, Rate A/50	144	°C	ISO 306
Vicat Softening Temp, Rate B/50	138	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience