NORYL N300XD resin is a 8% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade contains non-halogen flame retardant and has good balance of strength and toughness. NORYL N300XD resin exhibits high heat resistance, dimensional stability, hydrolytic stability, and low moisture absorption. This material is intended for appliance internals, indoor and outdoor electrical enclosures / housings / connectors.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant | |||
| – 1.9 GHz | 2.74 | - | SABIC method |
| – 5 GHz | 2.72 | - | SABIC method |
| – 10 GHZ | 2.75 | - | SABIC method |
| Dissipation Factor | |||
| – 1.9 GHz | 0.00376 | - | SABIC method |
| – 5 GHz | 0.00516 | - | SABIC method |
| – 10 GHz | 0.00390 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 6.0 - 6.6 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 105 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 11.2 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Front - Zone 3 Temperature | 270 - 310 | °C | |
| Middle - Zone 2 Temperature | 260 - 305 | °C | |
| Rear - Zone 1 Temperature | 250 - 300 | °C | |
| Mold Temperature | 70 - 110 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 72 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.1 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3650 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3450 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 72 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3750 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 120 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3460 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.14 | - | ASTM D792 |
| Melt Flow Rate, 300°C/5.0 kgf | 12 | g/10 min | ASTM D1238 |
| Water Absorption, (23°C/24hrs) | 0.08 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.65 - 0.8 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.8 - 0.95 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 133 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 125 | °C | ASTM D648 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |