NORYL™ NCF1010 is a compound based on PPE+PS resin containing 10% Glass Fiber, 10% Carbon Fiber and 10% PTFE. Added features: Structural and Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 300 - 305 | °C | |
| Front - Zone 3 Temperature | 300 - 310 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 275 - 290 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 97 | MPa | SABIC - Japan Method |
| Tensile Strain, break | 7 - 7 | % | SABIC - Japan Method |
| Flexural Stress | 129 | MPa | ASTM D790 |
| Flexural Modulus | 7610 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.21 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.06 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 - 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.8 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 134 | °C | ASTM D648 |
| CTE, -30°C to 30°C | 2.5E-05 - 4.5E-05 | 1/°C | TMA |