NORYL NH5120 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm. NORYL NH5120 resin offers a good balance of heat, flow, hydrolytic stability, low creep and dimensional stability along with mechanical property retention in tough outdoor environments. This material is an excellent candidate for outdoor housings / enclosures, HVAC components, and photovoltaic / solar junction box applications.
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Yellow Card Link 2 | View | - | - |
| UL Recognized, 94V-1 Flame Class Rating | ≥1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.0 mm | 725 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.5 mm | 725 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 2.0 mm | 700 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 186 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 111 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 53 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 12 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 17 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Front - Zone 3 Temperature | 270 - 310 | °C | |
| Middle - Zone 2 Temperature | 260 - 305 | °C | |
| Rear - Zone 1 Temperature | 250 - 300 | °C | |
| Mold Temperature | 75 - 105 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 70 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 29 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2610 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 105 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2680 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 9.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2650 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 105 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2610 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.1 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate, 280°C/5.0 kgf | 12.2 | g/10 min | ASTM D1238 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.25 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 11 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 136 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 131 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 116 | °C | ASTM D648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 134 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 123 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 8.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.7E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 8.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.7E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 136 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 138 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 110 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.