NORYL™ Resin NHP6024

NORYL NHP6024 resin is a 20% glass reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant UL94 flame rating of V0 at 1.5mm. NORYL NHP6024 is based on a unique co-polymer technology and exhibits high flow, high impact resistance, dimensional stability, hydrolytic stability, strong electrical performance, very low moisture absorption and specific gravity. The target applications are electrical components, electric vehicle (EV) battery modules and energy storage.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Good Processability
High Flow
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
Non Cl/Br flame retardant

Industry

Material previously used in

Energy Storage

Applications

Possible usage of material

Electrical Components & Infrastructure
EV/HEV Battery

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	4.0E+16	Ω	ASTM D257
Volume Resistivity	1.9E+17	Ω.cm	ASTM D257
Dielectric Strength, in oil, 2.0 mm	26.8	kV/mm	IEC 60243-1

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
UL Recognized, 94-5VA Flame Class Rating	≥2.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	100	J/m	ASTM D256
Izod Impact, unnotched, 23°C	480	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	32	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	34	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	105 - 110	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 310	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	270 - 310	°C
Middle - Zone 2 Temperature	260 - 305	°C
Rear - Zone 1 Temperature	250 - 300	°C
Mold Temperature	75 - 105	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 70	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	113	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	110	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	2	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D638
Tensile Modulus, 5 mm/min	6600	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	155	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	6080	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	110	MPa	ISO 527
Tensile Stress, break, 5 mm/min	100	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2	%	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	6530	MPa	ISO 527
Flexural Strength, 2 mm/min	160	MPa	ISO 178
Flexural Modulus, 2 mm/min	6270	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.24	-	ASTM D792
Density	1.24	g/cm³	ISO 1183
Melt Flow Rate, 300°C/5.0 kgf	26	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/10.0 kg	30	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.07	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.03	%	ISO 62-4
Mold Shrinkage, flow	0.25 - 0.35	%	SABIC method
Mold Shrinkage, xflow	0.60 - 0.70	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	138	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	126	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	134	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	127	°C	ISO 75/Af
CTE
– -40°C to 120°C, flow	2.1E-05	1/°C	ASTM D648
– -40°C to 120°C, xflow	7.7E-05	1/°C	ASTM D648
– -40°C to 120°C, flow	2.1E-05	1/°C	ISO 11359-2
– -40°C to 120°C, xflow	7.7E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	137	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	142	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	135	°C	ISO 306
Vicat Softening Temp, Rate B/120	139	°C	ISO 306
Relative Temp Index, Elec	65	°C	UL 746B
Relative Temp Index, Mech w/impact	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	65	°C	UL 746B

THIS SITE USES COOKIES

NORYL™ Resin NHP6024

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

NORYL™ Resin NHP6024

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL