NORYL™ Resin NHP8000VT3

NORYL NHP8000VT3 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance, ultra-thin-wall FR and High tracking resistance performance. This extrusion and injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries CTI 600V / PLC 0 and UL94 flame rating of V0 at 0.25mm. NORYL NHP8000VT3 is based on a unique co-polymer technology and exhibits high impact, high heat resistance, dimensional stability, hydrolytic stability, strong electrical performance, low moisture absorption and low specific gravity. This grade is targeted for electrical vehicle (EV) battery pack insulation sheet/film, bus bar insulation layer and other high voltage electric components.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding
Extrusion
Thermoforming

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
Good Processability
Heat Stabilized
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Automotive EV
Energy Storage

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	7.50E+16	Ω	ASTM D257
Volume Resistivity	6.20E+15	Ω.cm	ASTM D257
Comparative Tracking Index (UL) {PLC}	0	PLC Code	UL 746A

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 4	Hrs
Barrel - Zone 1 Temperature	210	°C
Barrel - Zone 2 Temperature	275	°C
Barrel - Zone 3 Temperature	280	°C
Barrel - Zone 4 Temperature	280	°C
Die Temperature	285	°C
Roll Stack Temperature - Bottom	20 - 30	°C
Roll Stack Temperature - Middle	120 - 130	°C
Roll Stack Temperature - Top	120 - 140	°C

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.25	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	211	J/m	ASTM D256
Izod Impact, notched, -40°C	84	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -40°C	1830	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	280 - 330	°C
Nozzle Temperature	250 - 330	°C
Front - Zone 3 Temperature	280 - 330	°C
Middle - Zone 2 Temperature	280 - 330	°C
Rear - Zone 1 Temperature	280 - 330	°C
Mold Temperature	70 - 120	°C
Back Pressure	0.3 - 0.8	MPa
Screw Speed	20 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	66.8	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4.2	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	10.8	%	ASTM D638
Tensile Modulus, 5 mm/min	2491	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	108	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2600	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.1	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.04	%	ISO 62-1
Melt Flow Rate, 300°C/5.0 kgf	11.7	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.73	%	SABIC method
Mold Shrinkage, xflow	0.79	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	150	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	133	°C	ASTM D648
Vicat Softening Temp, Rate A/50	166	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	155	°C	ASTM D1525
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum	140	°C	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES