NORYL™ Resin NHP8010T3

NORYL NHP8010T3 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance and ultra-thin-wall FR. This extrusion and injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries UL94 flame rating of V0 at 0.3mm. NORYL NHP8010T3 is based on a unique co-polymer technology and exhibits high impact, high heat resistance, dimensional stability, hydrolytic stability, strong electrical performance, low moisture absorption and low specific gravity. This grade is targeted for electrical vehicle (EV) battery pack insulation sheet/film, bus bar insulation layer and other high voltage electric component. See NHP8000VT3 resin for V0 at 0.25mm and CTI 600V/PLC 0 version.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding
Extrusion
Thermoforming

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
Good Processability
Heat Stabilized
High temperature resistance
Hydrolytic Stability
Impact resistant
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Automotive EV
Energy Storage

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	6.60E+16	Ω	ASTM D257
Volume Resistivity	4.64E+16	Ω.cm	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.3	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	326	J/m	ASTM D256
Izod Impact, notched, -40°C	103	J/m	ASTM D256
Izod Impact, unnotched, 23°C	2190	J/m	ASTM D4812
Izod Impact, unnotched, -40°C	1750	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	25	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -40°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	NB	kJ/m²	ISO 180/1U

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	280 - 320	°C
Nozzle Temperature	250 - 320	°C
Front - Zone 3 Temperature	280 - 320	°C
Middle - Zone 2 Temperature	280 - 320	°C
Rear - Zone 1 Temperature	280 - 320	°C
Mold Temperature	70 - 120	°C
Back Pressure	0.3 - 0.8	MPa
Screw Speed	20 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	62	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	49	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4.2	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	10.6	%	ASTM D638
Tensile Modulus, 5 mm/min	2382	MPa	ASTM D638
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span	102	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	106	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	104	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2470	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	63	MPa	ISO 527
Tensile Stress, break, 5 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4.2	%	ISO 527
Tensile Strain, break, 5 mm/min	35.6	%	ISO 527
Tensile Modulus, 1 mm/min	2436	MPa	ISO 527
Flexural Strength, 2 mm/min	106	MPa	ISO 178
Flexural Modulus, 2 mm/min	2452	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.09	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.04	%	ISO 62-4
Melt Flow Rate, 300°C/5.0 kgf	15.7	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.77	%	SABIC method
Mold Shrinkage, xflow	0.76	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	149	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	132	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	149	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	134	°C	ISO 75/Af
Vicat Softening Temp, Rate A/50	163	°C	ASTM D1525
Vicat Softening Temp, Rate A/120	165	°C	ASTM D1525

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES