NORYL™ Resin NP6100

NORYL NP6100 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance with good strength, toughness and robust FR performance. This extrudable grade contains non-brominated, non-chlorinated flame retardant. NORYL NP6100 resin may be an excellent candidate for mining pipe applications as well as low smoke cable channel applications where EN45545 R22 certificate ( European railway standard for small electrical parts) is required.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Asia
Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
High temperature resistance
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Electrical
Rail

Applications

Possible usage of material

Enclosure/Housing/Cover

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Adapter Temperature	255 - 275	°C
Die Temperature	255 - 275	°C

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-1 Flame Class Rating	1.5	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Smoke density, DS-max, 25 kW/m2, 1.5 mm	47	-	ISO 5659-2

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	510	J/m	ASTM D256
Izod Impact, notched, -30°C	180	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	39.9	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	15.8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	37	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	21	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255 - 275	°C
Rear - Zone 1 Temperature	235 - 255	°C
Middle - Zone 2 Temperature	255 - 275	°C
Front - Zone 3 Temperature	255 - 275	°C
Nozzle Temperature	255 - 275	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	47	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	10.5	%	ASTM D638
Flexural Stress, yield, 6.4 mm	95	MPa	ASTM D790
Flexural Modulus, 6.4 mm	2200	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	68	MPa	ISO 527
Tensile Stress, break, 50 mm/min	52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4.5	%	ISO 527
Tensile Strain, break, 50 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	2330	MPa	ISO 527
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	77	MPa	ISO 178
Flexural Stress, break, 2 mm/min	100	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	60	MPa	ASTM D638

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Melt Flow Rate, 280°C/10.0 kgf	10.5	g/10 min	ASTM D1238
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.5 - 0.7	%	SABIC method
Melt Volume Rate, MVR at 280°C/10.0 kg	11	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	146	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
Vicat Softening Temp, Rate B/120	153	°C	ISO 306

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Adapter Temperature	255 - 275	°C
Die Temperature	255 - 275	°C

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-1 Flame Class Rating	1.5	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Smoke density, DS-max, 25 kW/m2, 1.5 mm	47	-	ISO 5659-2

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	510	J/m	ASTM D256
Izod Impact, notched, -30°C	180	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	39.9	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	15.8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	37	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	21	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255 - 275	°C
Rear - Zone 1 Temperature	235 - 255	°C
Middle - Zone 2 Temperature	255 - 275	°C
Front - Zone 3 Temperature	255 - 275	°C
Nozzle Temperature	255 - 275	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	47	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	10.5	%	ASTM D638
Flexural Stress, yield, 6.4 mm	95	MPa	ASTM D790
Flexural Modulus, 6.4 mm	2200	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	68	MPa	ISO 527
Tensile Stress, break, 50 mm/min	52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4.5	%	ISO 527
Tensile Strain, break, 50 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	2330	MPa	ISO 527
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	77	MPa	ISO 178
Flexural Stress, break, 2 mm/min	100	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	60	MPa	ASTM D638

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Melt Flow Rate, 280°C/10.0 kgf	10.5	g/10 min	ASTM D1238
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.5 - 0.7	%	SABIC method
Melt Volume Rate, MVR at 280°C/10.0 kg	11	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	146	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
Vicat Softening Temp, Rate B/120	153	°C	ISO 306

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Adapter Temperature	255 - 275	°C
Die Temperature	255 - 275	°C

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-1 Flame Class Rating	1.5	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Smoke density, DS-max, 25 kW/m2, 1.5 mm	47	-	ISO 5659-2

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	510	J/m	ASTM D256
Izod Impact, notched, -30°C	180	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	39.9	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	15.8	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	37	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	21	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	255 - 275	°C
Rear - Zone 1 Temperature	235 - 255	°C
Middle - Zone 2 Temperature	255 - 275	°C
Front - Zone 3 Temperature	255 - 275	°C
Nozzle Temperature	255 - 275	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	47	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	10.5	%	ASTM D638
Flexural Stress, yield, 6.4 mm	95	MPa	ASTM D790
Flexural Modulus, 6.4 mm	2200	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	68	MPa	ISO 527
Tensile Stress, break, 50 mm/min	52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4.5	%	ISO 527
Tensile Strain, break, 50 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	2330	MPa	ISO 527
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	77	MPa	ISO 178
Flexural Stress, break, 2 mm/min	100	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	60	MPa	ASTM D638

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Melt Flow Rate, 280°C/10.0 kgf	10.5	g/10 min	ASTM D1238
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.5 - 0.7	%	SABIC method
Melt Volume Rate, MVR at 280°C/10.0 kg	11	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	121	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	146	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	151	°C	ISO 306
Vicat Softening Temp, Rate B/120	153	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

NORYL™ Resin NP6100

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

EXTRUSION

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

EXTRUSION

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

EXTRUSION

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL