NORYL™ Resin PCN2910

NORYL PCN2910 resin is a 35% glass fiber and mineral reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high modulus, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VB at 2.3mm, V0 at 3mm, and V1 at 1.5mm. NORYL PCN2910 resin exhibits good dimensional stability, low specific gravity, and Low Warpage. It is an excellent candidate for printer chassis applications where high modulus and tight tolerance molding are required.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
High stiffness/Strength
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Building Component
Electrical
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Circuit Protection
Data Management
Document Handling
Electronic Components
Enclosure/Housing/Cover
Enclosures
Security/Detection
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94-5VB Flame Class Rating	≥2.3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	3	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	331	J/m	ASTM D4812
Izod Impact, notched, 23°C	68	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	7	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	14	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
Charpy Impact, notched, 23°C	4	kJ/m²	ISO 179/2C
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	20	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	105 - 110	°C
Drying Time	3 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	295 - 315	°C
Front - Zone 3 Temperature	280 - 315	°C
Middle - Zone 2 Temperature	270 - 310	°C
Rear - Zone 1 Temperature	260 - 305	°C
Mold Temperature	75 - 105	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 70	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	123	MPa	ASTM D638
Tensile Stress, brk, Type I, 10 mm/min	115	MPa	SABIC - Japan Method
Tensile Strain, brk, Type I, 5 mm/min	1.5	%	ASTM D638
Tensile Strain, yld, Type I, 10 mm/min	5	%	SABIC - Japan Method
Tensile Modulus, 5 mm/min	11370	MPa	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	159	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	8940	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	106	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	10600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	160	MPa	ISO 178
Flexural Modulus, 2 mm/min	9130	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.38	-	ASTM D792
Mold Shrinkage, flow	0.25 - 0.3	%	SABIC method
Melt Flow Rate, 300°C/2.16 kgf	11	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	140	°C	ASTM D1525
HDT, 1.82 MPa, 6.4 mm, unannealed	125	°C	ASTM D648
CTE, -30°C to 30°C	0.000021 - 0.000033	1/°C	TMA
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	129	°C	ISO 75/Af
Relative Temp Index, Elec	65	°C	UL 746B
Relative Temp Index, Mech w/impact	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	65	°C	UL 746B

Register for High value Multi-Point Data