NORYL PKN4775F resin is a non-reinforced, opaque blend of polyphenylene ether (PPE) + polystyrene (PS) and is FDA food compliant in several colors. This high heat, thin wall extrusion and injection moldable grade is an improved version of NORYL PKN4775F resin and exhibits modulus at elevated temperature and good chemical resistance. NORYL PKN4775F resin is targeted for applications in high performance packaging.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 268 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 161 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 39 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 11 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 19 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 47 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 35 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2120 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 78 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2210 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.2 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 29.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2120 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 82 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2160 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.05 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | SABIC method |
| Melt Flow Rate, 300°C/5.0 kgf | 15.3 | g/10 min | ASTM D1238 |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.25 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 14 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Barrel - Zone 1 Temperature | 205 - 225 | °C | |
| Barrel - Zone 2 Temperature | 215 - 240 | °C | |
| Barrel - Zone 3 Temperature | 240 - 265 | °C | |
| Barrel - Zone 4 Temperature | 240 - 265 | °C | |
| Adapter Temperature | 240 - 265 | °C | |
| Die Temperature | 240 - 265 | °C | |
| Roll Stack Temp - Top | 105 - 120 | °C | |
| Roll Stack Temp - Middle | 105 - 120 | °C | |
| Roll Stack Temp - Bottom | 105 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 142 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 122 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 9.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | N/A | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 142 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |