IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 197 | J/m | ASTM D256 |
Izod Impact, notched, -40°C | 133 | J/m | ASTM D256 |
NORYL PX0888 resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This grade exhibits very low moisture absorption, hydrolytic stability, dimensional stabilty, good foam adhesion, and property retention over a wide temperature range. NORYL PX0888 resin is inherently UL94 HB and is an excellent candidate for automotive interior applications such as instrument panels, audio components, speaker housings, and interior trim.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 197 | J/m | ASTM D256 |
Izod Impact, notched, -40°C | 133 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 105 - 110 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 280 - 310 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 270 - 310 | °C | |
Middle - Zone 2 Temperature | 260 - 305 | °C | |
Rear - Zone 1 Temperature | 250 - 300 | °C | |
Mold Temperature | 75 - 105 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 30 | % | ASTM D638 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 93 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 2350 | MPa | ASTM D790 |
Hardness, Rockwell R | 118 | - | ASTM D785 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.04 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.1 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Volume Rate, MVR at 300°C/2.16 kg | 6 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 127 | °C | ASTM D648 |
CTE, 0°C to 100°C, flow | 7.38E-05 | 1/°C | ASTM E831 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 197 | J/m | ASTM D256 |
Izod Impact, notched, -40°C | 133 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 105 - 110 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 280 - 310 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 270 - 310 | °C | |
Middle - Zone 2 Temperature | 260 - 305 | °C | |
Rear - Zone 1 Temperature | 250 - 300 | °C | |
Mold Temperature | 75 - 105 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 30 | % | ASTM D638 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 93 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 2350 | MPa | ASTM D790 |
Hardness, Rockwell R | 118 | - | ASTM D785 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.04 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.1 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Volume Rate, MVR at 300°C/2.16 kg | 6 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 127 | °C | ASTM D648 |
CTE, 0°C to 100°C, flow | 7.38E-05 | 1/°C | ASTM E831 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Compliant, 94HB Flame Class Rating | 1.6 | mm | UL 94 by SABIC-IP |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 120 | °C | |
Drying Time | 2 - 3 | Hrs | |
Melt Temperature | 280 - 320 | °C | |
Nozzle Temperature | 280 - 310 | °C | |
Front - Zone 3 Temperature | 280 - 310 | °C | |
Middle - Zone 2 Temperature | 260 - 300 | °C | |
Rear - Zone 1 Temperature | 250 - 300 | °C | |
Mold Temperature | 80 - 120 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
Ball Indentation Hardness, H358/30 | 130 | MPa | ISO 2039-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.06 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 5 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate A/50 | 150 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 130 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | °C | ISO 75/Ae |