NORYL™ Resin PX2935

NORYL PX2935 resin is a 20% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This high impact extrusion grade exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for industrial applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
High stiffness/Strength
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Material Handling

Applications

Possible usage of material

Tray

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	99	J/m	ASTM D256

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	82	MPa	SABIC - Japan Method
Tensile Strain, break	4 - 6	%	SABIC - Japan Method
Flexural Stress	133	MPa	ASTM D790
Flexural Modulus	5590	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.06	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.4	%	SABIC method
Melt Flow Rate, 300°C/5.0 kgf	29.3	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 6.4 mm, unannealed	125	°C	ASTM D648
CTE, -30°C to 30°C	0.000022 - 0.000071	1/°C	TMA

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES