NORYL PX500 is an unfilled modified polyphenylene ether resin capable of multiple conversion routes. This resin is designed for lower odor during conversion than many standard modified PPE resins. NORYL PX500 provides an exceptional balance of high heat performance and dimensional stability with flow and may be an excellent material candidate for IC tray applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 58 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 300 - 325 | °C | |
| Nozzle Temperature | 300 - 325 | °C | |
| Front - Zone 3 Temperature | 290 - 325 | °C | |
| Middle - Zone 2 Temperature | 275 - 320 | °C | |
| Rear - Zone 1 Temperature | 265 - 315 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 70 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 71 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.4 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 35 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2400 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2590 | MPa | ASTM D790 |
| Hardness, Shore D, 30S reading | 82 | - | ASTM D2240 |
| Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5.1 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 5.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 110 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2530 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.06 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.8 - 0.9 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.8 - 0.9 | % | SABIC method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.23 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 320°C/5.0 kg | 21 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 192 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 170 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.9E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 7.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.9E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 192 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 193 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 169 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature