NORYL PX5534 resin is a 30% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade exhibits high heat resistance, low warpage, low moisture absorption, and dimensional stability. This material is an excellent candidate for applications such as central heating parts, water filters, and water meter components.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 590 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 20 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 300 - 325 | °C | |
| Nozzle Temperature | 300 - 325 | °C | |
| Front - Zone 3 Temperature | 290 - 325 | °C | |
| Middle - Zone 2 Temperature | 275 - 320 | °C | |
| Rear - Zone 1 Temperature | 265 - 315 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Shot to Cylinder Size | 30 - 70 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 130 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8600 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7200 | MPa | ASTM D790 |
| Tensile Stress, break, 50 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.31 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.4 | % | SABIC method |
| Melt Flow Rate, 280°C/5.0 kgf | 3.2 | g/10 min | ASTM D1238 |
| Water Absorption, (23°C/saturated) | 0.1 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.04 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 2 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 147 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 147 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 139 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.1E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.5E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7E-5 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 147 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 149 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 139 | °C | ISO 75/Af |