NORYL™ Resin PX9406V

NORYL PX9406V resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) and exhibits an excellent balance of non-brominated, non-chlorinated flame retardance, high heat resistance, low moisture absorption, good flow, and low specific gravity for light weight parts. This injection moldable grade carries UL94 flame ratings of V0 at 1.5mm along with a UL746C Outdoor Suitability rating of f1. NORYL PX9406V resin is targeted for applications such as solar/PV junction boxes, optimizers, micro-invertors and electrical enclosures.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Non Cl/Br flame retardant

Industry

Material previously used in

Building Component
Electrical
Electronic Components
Energy Management
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Air Conditioning
Enclosure/Housing/Cover
Gas/Electric Oven
Refrigerator
Washing Machine

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.0E+16	Ω.cm	ASTM D257
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 2	1.5	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	≥3.0	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 1	≥1.5	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94
UL Recognized, 94-5VA Flame Class Rating	≥3.0	mm	UL 94
UV-light, water exposure/immersion	f1	-	UL 746C
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.5 mm	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	800	°C	IEC 60695-2-13

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	221	J/m	ASTM D256
Izod Impact, notched, -30°C	87	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	20	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	8	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	21	kJ/m²	ISO 179/1eA
Instrumented Dart Impact Total Energy, 23°C	38	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	300 - 330	°C
Nozzle Temperature	300 - 330	°C
Front - Zone 3 Temperature	290 - 330	°C
Middle - Zone 2 Temperature	280 - 330	°C
Rear - Zone 1 Temperature	270 - 330	°C
Mold Temperature	80 - 120	°C
Back Pressure	0.03 - 0.08	MPa
Screw Speed	20 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	69	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	50	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.1	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	39	%	ASTM D638
Tensile Modulus, 5 mm/min	2270	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	102	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2500	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	69	MPa	ISO 527
Tensile Stress, break, 50 mm/min	59	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.0	%	ISO 527
Tensile Strain, break, 50 mm/min	9.1	%	ISO 527
Tensile Modulus, 1 mm/min	2450	MPa	ISO 527
Flexural Strength, 2 mm/min	111	MPa	ISO 178
Flexural Modulus, 2 mm/min	2510	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.09	-	ASTM D792
Density	1.09	g/cm³	ISO 1183
Melt Flow Rate, 300°C/5.0 kgf	10.7	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/5.0 kg	10	cm³/10 min	ISO 1133
Water Absorption, (23°C/saturated)	0.24	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.04	%	ISO 62
Mold Shrinkage, flow	0.5 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	139	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	140	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	160	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	161	°C	ISO 306
Vicat Softening Temp, Rate B/120	152	°C	ISO 306
CTE, -40°C to 40°C, flow	8.16E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.15E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	8.16E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.15E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES