FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Radiant Panel Listing | RP100 | - | UL Tested |
SINGLE LOT DATA. PPE+PS. Improved productivity and reliability. Nonchlorinated, nonbrominated flame retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Radiant Panel Listing | RP100 | - | UL Tested |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 165 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 90 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 28 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 53 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 7.9 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 36.1 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 104 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2750 | MPa | ASTM D790 |
Hardness, Rockwell R | 121 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 7.7 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 16.8 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2720 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 103 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2490 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.07 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/5.0 kgf | 35.9 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 147 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 128 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 113 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 132 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 121 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.08E-04 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 1.12E-04 | 1/°C | ASTM E831 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 130 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | °C | ISO 75/Ae |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 180 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 55 | MPa | SABIC - Japan Method |
Tensile Strain, break | 54 | % | SABIC - Japan Method |
Flexural Stress | 86 | MPa | ASTM D790 |
Flexural Modulus | 2450 | MPa | ASTM D790 |
Hardness, Rockwell R | 119 | - | ASTM D785 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.1 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 250°C/10.0 kgf | 4.7 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 6.4 mm, unannealed | 123 | °C | ASTM D648 |
CTE, -30°C to 30°C | 6.00E-05 | 1/°C | TMA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+15 | Ω.cm | IEC 60093 |
Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
Dissipation Factor, 50/60 Hz | 0.004 | - | IEC 60250 |
Dissipation Factor, 1 MHz | 0.002 | - | IEC 60250 |
Comparative Tracking Index | 200 | V | IEC 60112 |
Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Recognized, 94V-1 Flame Class Rating | 0.75 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 6 | mm | UL 94 |
Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
Oxygen Index (LOI) | 31 | % | ISO 4589 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 7 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 - 100 | °C | |
Drying Time | 2 - 3 | Hrs | |
Melt Temperature | 280 - 300 | °C | |
Nozzle Temperature | 260 - 280 | °C | |
Front - Zone 3 Temperature | 280 - 300 | °C | |
Middle - Zone 2 Temperature | 260 - 280 | °C | |
Rear - Zone 1 Temperature | 240 - 260 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 90 - 120 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 10 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
Ball Indentation Hardness, H358/30 | 95 | MPa | ISO 2039-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
Density | 1.11 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.23 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
Melt Volume Rate, MVR at 280°C/5.0 kg | 7 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Ball Pressure Test, approximate maximum | 125 | °C | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 140 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 130 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 130 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 120 | °C | ISO 75/Ae |
Relative Temp Index, Elec | 110 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 110 | °C | UL 746B |